SPECIFICATION
• Supplier : Samsung electro-mechanics • Samsung P/N : CL32A106KOMLNNE
• Product : Multi-layer Ceramic Capacitor •Description : CAP, 10㎌, 16V, ±10%, X5R, 1210
CL 32 A 106 K O M L N N E
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 1210 (inch code) L: 3.2 ± 0.3 mm W: ± 0.2 mm
⑧Thickness division Low profile
③Dielectric X5R Inner electrode
④Capacitance 10 ㎌Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 16 V ⑩Special Reserved for future use
⑦Thickness 1.15 ± 0.1 mm ⑪Packaging Embossed Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2 Vrms
Tan δ (DF) 0.1 max.
Insulation 10,000Mohm or 100Mohm⋅㎌Rated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (×10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X5R
Characterisitcs (From -55℃ to 85℃, Capacitance change shoud be within ±15%)
Adhesive Strength No peeling shall be occur on the 500g⋅F, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface 1) Sn63Pb37 solder
is to be soldered newly 235±5℃, 5±0.5sec.
2) SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Performance Test condition
250%
A. Samsung Part Number
Sn 100%
Cu
Ni
2.5
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours × 3 direction (x, y, z)
Humidity Capacitance change : within ±12.5% 40±2℃, 90~95%RH, 500+12/-0hrs
Tan δ : 0.125 max
IR : 25㏁·㎌ or Over
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0hrs
IR : 12.5㏁·㎌ or Over
High Temperature Capacitance change : within ±12.5% With 150% of The rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : 25㏁·㎌ or Over
1000+48/-0hrs
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperatur
e
→25℃
→Max. operating temperature →25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
Performance Test condition