SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL10C220JB8NNNL CAP, 22, 50V, 5%, C0G, 0603 Description : Product : Multi-layer Ceramic Capacitor A. Samsung Part Number Series CL 10 C 220 J B 8 N N N L Samsung Multi-layer Ceramic Capacitor Size 0603 Dielectric C0G (inch code) L: 1.6 0.1 22 5 % Capacitance Capacitance tolerance Rated Voltage 50 V Thickness 0.8 0.1 mm mm 0.8 0.1 mm W: Inner electrode Ni Termination Cu Plating Sn 100% (Pb Free) Product Normal Special Reserved for future use Packaging Cardboard Type, 13" reel B. Samsung Reliability Test and Judgement condition Performance Within specified tolerance Test condition 110% 0.5~5Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (10) 300% of the rated voltage Voltage mechanical breakdown Temperature C0G Characteristics Adhesive Strength (From -55 to 125, Capacitance change should be within 30PPM/) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. Solderability within 5% or 0.5 whichever is larger More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. Capacitance 840 min Q Insulation (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec. Solder pot : 2705, 101sec. Performance Test condition Vibration Test Capacitance change : Moisture within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours 3 direction (x, y, z) Capacitance change : With rated voltage Resistance within 7.5% or 0.75 whichever is larger 402, 90~95%RH, 500+12/-0hrs Q: 173.33 min IR : High Temperature Resistance Amplitude : 1.5mm 500Mohm or 25Mohm Whichever is Smaller Capacitance change : With 200% within 3% or 0.3 whichever is larger Q: 330 min Max. operating temperature IR : of the rated voltage 1000+48/-0hrs 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : 1 cycle condition Cycling within 2.5% or 0.25 whichever is larger Min. operating temperature Tan , IR : initial spec. Max. operating temperature 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue. 25 25