AC1206KKX7R0BB105 - YAGEO - searchdatasheet.com

85

Product Specification – February 26, 2019 V.12

DATA SHEET

SURFACE MOUNT MULTILAYER

CERAMIC CAPACITORS

Automotive grade

NP0/X7R

6.3 V TO 630 V

0.2 pF to 2.2 µF

RoHS compliant & Halogen Free

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

2

24

Product specification

ORDERING INFORMATION - GLOBAL PART NUMBER

All part numbers are identified by the series, size, tolerance, TC material,

packing style, voltage, process code, termination and capacitance value.

GLOBAL PART NUMBER

AC

XXXX X X XXX X

B

X XXX

(1) (2) (3) (4) (5) (6) (7)

(1) SIZE – INCH BASED (METRIC)

0201 (0603) / 0402 (1005) / 0603 (1608) / 0805 (2012) / 1206 (3216)/ 1210 (3225) /

0508 (1220) / 0612 (1632)

(2) TOLERANCE

B = ± 0.1 pF

C = ± 0.25 pF

D = ± 0.5 pF

F = ± 1%

G = ± 2%

J = ± 5%

K = ± 10%

M = ± 20%

(3) PACKING STYLE

R = Paper/PE taping reel; Reel 7 inch

K = Blister taping reel; Reel 7 inch

P = Paper/PE taping reel; Reel 13 inch

F = Blister taping reel; Reel 13 inch

(4) TC MATERIAL

NPO

X7R

(5) RATED VOLTAGE

5 = 6.3 V

6 = 10 V

7 = 16 V

8 = 25 V

9 = 50 V

0 = 100 V

A = 200 V

Y = 250 V

B = 500 V

Z = 630 V

(6) PROCESS

N = NP0

B = Class 2 MLCC

(7) CAPACITANCE VALUE

2 significant digits+number of zeros

The 3rd digit signifies the multiplying factor, and letter R is decimal point

Example: 121 = 12 x 101 = 120 pF

SCOPE

This specification describes

Automotive grade NP0/X7R series

chip capacitors with lead-free

terminations and used for

automotive equipments.

APPLICATIONS

All general purpose applications

Entertainment applications

Comfort / security applications

Information applications

FEATURES

 AEC-Q200 qualified

 MSL class: MSL 1

 AC series soldering is

compliant with J-STD-020D

 Halogen free epoxy

 RoHS compliant

 Reduce environmentally

hazardous waste

 High component and

equipment reliability

 Save PCB space

 The capacitors are 100%

performed by automatic optical

inspection prior to taping.

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

3

24

Product specification

CONSTRUCTION

The capacitor consists of a

rectangular block of ceramic

dielectric in which a number of

interleaved metal electrodes are

contained. This structure gives

rise to a high capacitance per

unit volume.

The inner electrodes are

connected to the two end

terminations and finally covered

with a layer of plated tin (Matte

Sn). The terminations are lead-

free. A cross section of the

structure is shown in Fig.1.

Fig. 1 Surface mounted multilayer ceramic capacitor construction

TYPE

L1 (mm)

W (mm)

T (MM)

L2 / L3 (mm)

L4 (mm)

min.

max.

min.

0201

0.6 ± 0.03

0.3 ± 0.03

Refer to

table 3 to 12

0.10

0.20

0402

1.0 ± 0.05

0.5 ± 0.05

0.15

0.30

0.40

0603

1.6 ± 0.10

0.8 ± 0.10

0.20

0.60

0.40

0805

2.0 ± 0.20

1.25 ± 0.20

0.25

0.75

0.70

1206

3.2 ± 0.30

1.6 ± 0.20

0.25

0.75

1.40

1210

3.2 ± 0.30

2.5 ± 0.20

0.25

0.75

1.40

1812

4.5± 0.40

3.2± 0.40

0.25

0.75

2.20

Table 1 For outlines see fig. 2

DIMENSION

O

OU

UT

TL

LI

IN

NE

ES

S

For dimension see Table 1

Fig. 2 Surface mounted multilayer

ceramic capacitor dimension

O

OU

UT

TL

LI

IN

NE

ES

S

For dimensions see Table 2

Fig. 3 Surface mounted multilayer ceramic capacitor dimension

TYPE

0508

(4 X 0402)

0612

(4 X 0603)

L (mm)

2.0 ± 0.15

3.2 ± 0.15

W (mm)

1.25 ± 0.15

1.60 ± 0.15

Tmin. (mm)

0.50

0.70

Tmax. (mm)

0.70

0.90

A (mm)

0.28 ± 0.10

0.4 ± 0.10

B (mm)

0.2 ± 0.10

0.3 ± 0.20

P (mm)

0.5 ± 0.10

0.8 ± 0.10

Table 2 For outlines see fig. 3

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

4

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR NP0

Table 3 Sizes from 0201 to 0805

CAP.

0201

0402

0603

0805

25 V / 50 V

50 V

100 V

250 V

50 V

100 V

250V

0.2 pF

0.3± 0.03

0.47 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.56 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.68 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.82 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

1.0 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

1.2 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

1.5 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

1.8 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

2.2 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

2.7 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

3.3 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

3.9 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

4.7 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

5.6 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

6.8 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

8.2 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

10 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

12 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

15 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

18 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

22 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

27 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

33 pF

0.3± 0.03

0.5± 0.05

0.8± 0.1

0.6± 0.1

39 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

47 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

56 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

68 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

82 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

100 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-12 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

5

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR NP0

Table 4 Sizes from 0402 to 0805 (continued)

CAP.

0402

0603

0805

50 V

100 V

250 V

50 V

100 V

250 V

120 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

150 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

180 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

220 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

270 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

330 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

390 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

470 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

560 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

680 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

820 pF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

1.0 nF

0.5± 0.05

0.8± 0.1

0.6± 0.1

0.85± 0.1

1.2 nF

0.85± 0.1

1.5 nF

0.85± 0.1

1.8 nF

0.85± 0.1

2.2 nF

1.25± 0.2

2.7 nF

1.25± 0.2

3.3 nF

1.25± 0.2

3.9 nF

1.25± 0.2

4.7 nF

1.25± 0.2

5.6 nF

1.25± 0.2

6.8 nF

1.25± 0.2

8.2 nF

1.25± 0.2

10 nF

1.25± 0.2

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-12 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

6

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR NP0

Table 5 Sizes from 1206 to 1210

CAP.

1206

1210

50 V

100 V

250 V

500 V

630 V

50 V

100 V

250 V

500 V

10 pF

0.6± 0.1

1.25± 0.2

12 pF

0.6± 0.1

1.25± 0.2

15 pF

0.6± 0.1

1.25± 0.2

18 pF

0.6± 0.1

1.25± 0.2

22 pF

0.6± 0.1

1.25± 0.2

27 pF

0.6± 0.1

1.25± 0.2

33 pF

0.6± 0.1

1.25± 0.2

39 pF

0.6± 0.1

1.25± 0.2

47 pF

0.6± 0.1

1.25± 0.2

56 pF

0.6± 0.1

1.25± 0.2

68 pF

0.6± 0.1

1.25± 0.2

82 pF

0.6± 0.1

1.25± 0.2

100 pF

0.6± 0.1

1.25± 0.2

120 pF

0.6± 0.1

1.25± 0.2

150 pF

0.6± 0.1

1.25± 0.2

180 pF

0.6± 0.1

1.25± 0.2

220 pF

0.6± 0.1

1.25± 0.2

270 pF

0.6± 0.1

1.25± 0.2

330 pF

0.6± 0.1

1.25± 0.2

390 pF

0.6± 0.1

1.25± 0.2

470 pF

0.6± 0.1

1.25± 0.2

560 pF

0.6± 0.1

1.25± 0.2

680 pF

0.6± 0.1

1.25± 0.2

820 pF

0.6± 0.1

0.85± 0.1

1.25± 0.2

1.0 nF

0.6± 0.1

0.85± 0.1

1.25± 0.2

1.2 nF

0.6± 0.1

0.85± 0.1

1.25± 0.2

1.5 nF

0.6± 0.1

0.85± 0.1

1.25± 0.2

1.8 nF

0.6± 0.1

1.25± 0.2

2.2 nF

0.6± 0.1

1.25± 0.2

2.7 nF

0.6± 0.1

1.25± 0.2

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-12 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

7

24

Product specification

Table 6 Sizes from 0201 to 0603

CAPACITANCE RANGE & THICKNESS FOR X7R

CAP.

0201

0402

0603

25V

50 V

10V

16 V

25 V

50 V

100 V

10V

16 V

25 V

50 V

100 V

100 pF

0.3± 0.03

150 pF

0.3± 0.03

220 pF

0.3± 0.03

0.5± 0.05

330 pF

0.3± 0.03

0.5± 0.05

470 pF

0.3± 0.03

0.5± 0.05

680 pF

0.3± 0.03

0.5± 0.05

1.0 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

1.5 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

2.2 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

3.3 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

4.7 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

6.8 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

10 nF

0.3± 0.03

0.5± 0.05

0.8± 0.1

15 nF

0.5± 0.05

0.8± 0.1

22 nF

0.5± 0.05

0.8± 0.1

33 nF

0.5± 0.05

0.8± 0.1

47 nF

0.5± 0.05

0.8± 0.1

68 nF

0.5± 0.05

0.8± 0.1

100 nF

0.5± 0.05

0.8± 0.1

150 nF

0.8± 0.1

220 nF

0.8± 0.1

330 nF

0.8± 0.1

470 nF

0.8± 0.1

680 nF

0.8± 0.1

1 µF

0.8± 0.1

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-6 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

8

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR X7R

Table 8 Size 0805

CAP.

0805

10 V

16 V

25 V

50 V

100 V

250 V

500 V

1.0 nF

0.85± 0.1

1.5 nF

0.85± 0.1

2.2 nF

0.85± 0.1

3.3 nF

0.85± 0.1

4.7 nF

0.85± 0.1

6.8 nF

0.85± 0.1

1.25± 0.2

10 nF

0.85± 0.1

1.25± 0.2

15 nF

0.85± 0.1

1.25± 0.2

22 nF

0.85± 0.1

1.25± 0.2

33 nF

0.85± 0.1

1.25± 0.2

47 nF

0.85± 0.1

1.25± 0.2

68 nF

0.85± 0.1

1.25± 0.2

100 nF

0.85± 0.1

1.25± 0.2

150 nF

0.85± 0.1

1.25± 0.2

220 nF

0.85± 0.1

1.25± 0.2

330 nF

1.25± 0.2

470 nF

1.25± 0.2

680 nF

1.25± 0.2

1 µF

1.25± 0.2

2.2 µF

1.25± 0.2

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-6 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

9

24

Product specification

Table 9 Size 1206

CAPACITANCE RANGE & THICKNESS FOR X7R

CAP.

1206

6.3 V

10V

16V

25V

50 V

100 V

250 V

22 nF

0.85± 0.1

1.25± 0.2

33 nF

0.85± 0.1

1.60± 0.2

47 nF

0.85± 0.1

1.60± 0.2

68 nF

0.85± 0.1

1.25± 0.2

1.60± 0.2

100 nF

0.85± 0.1

1.25± 0.2

1.60± 0.2

150 nF

0.85± 0.1

1.25± 0.2

220 nF

0.85± 0.1

1.25± 0.2

330 nF

0.85± 0.1

1.60± 0.2

470 nF

1.00± 0.1

1.60± 0.2

680 nF

1.15± 0.1

1.60± 0.2

1 µF

1.15± 0.1

1.60± 0.2

2.2 µF

1.60± 0.2

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-6 series is on request

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

10

24

Product specification

CAP.

1210

1812

6.3V

10 V

16 V

25 V

50V

100 V

250 V

50V

100V

100 nF

0.85± 0.1

1.25± 0.2

150 nF

0.85± 0.1

1.25± 0.2

220 nF

0.85± 0.1

1.25± 0.2

330 nF

0.85± 0.1

1.25± 0.2

2.0± 0.2

470 nF

1.25± 0.2

2.0± 0.2

1.60± 0.2

680 nF

1.25± 0.2

2.0± 0.2

1.60± 0.2

1 µF

1.25± 0.2

2.0± 0.2

1.60± 0.2

2.2 µF

2.0± 0.2

4.7 µF

2.5± 0.2

NOTE

1. Values in shaded cells indicate thickness class in mm

2. Capacitance value of non E-6 series is on request

CAPACITANCE RANGE & THICKNESS FOR X7R

Table 10 Size 1210

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

11

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR 4C-ARRAY

Table 11 Temperature characteristic material from NP0

CAPACITANCE

0508 (4 x 0402)

0612 (4 x 0603)

50 V

10 pF

0.6± 0.1

0.8± 0.1

15 pF

0.6± 0.1

0.8± 0.1

18 pF

0.6± 0.1

0.8± 0.1

22 pF

0.6± 0.1

0.8± 0.1

33 pF

0.6± 0.1

0.8± 0.1

39 pF

0.6± 0.1

0.8± 0.1

47 pF

0.6± 0.1

0.8± 0.1

56 pF

0.6± 0.1

0.8± 0.1

68 pF

0.6± 0.1

0.8± 0.1

82 pF

0.6± 0.1

0.8± 0.1

100 pF

0.6± 0.1

0.8± 0.1

120 pF

0.8± 0.1

150 pF

0.8± 0.1

180 pF

0.8± 0.1

220 pF

0.8± 0.1

270 pF

0.8± 0.1

330 pF

0.8± 0.1

390 pF

0.8± 0.1

470 pF

0.8± 0.1

560 pF

680 pF

820 pF

1.0 nF

NOTE

Values in shaded cells indicate thickness class in mm

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

12

24

Product specification

CAPACITANCE RANGE & THICKNESS FOR 4C-ARRAY

Table 12 Temperature characteristic material from X7R

CAPACITANCE

0508 (4 x 0402)

0612 (4 x 0603)

16 V

25 V

50 V

16 V

25 V

50 V

220 pF

0.8± 0.1

330 pF

0.8± 0.1

470 pF

0.8± 0.1

680 pF

0.8± 0.1

1.0 nF

0.6± 0.1

0.8± 0.1

1.5 nF

0.6± 0.1

0.8± 0.1

2.2 nF

0.6± 0.1

0.8± 0.1

3.3 nF

0.6± 0.1

0.8± 0.1

4.7 nF

0.6± 0.1

0.8± 0.1

6.8 nF

0.6± 0.1

0.8± 0.1

10 nF

0.6± 0.1

0.8± 0.1

15 nF

0.6± 0.1

0.8± 0.1

22 nF

0.6± 0.1

0.8± 0.1

33 nF

0.6± 0.1

0.8± 0.1

47 nF

0.6± 0.1

0.8± 0.1

68 nF

0.6± 0.1

100 nF

0.6± 0.1

NOTE

Values in shaded cells indicate thickness class in mm

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

13

24

Product specification

Table 13

THICKNESS CLASSES AND PACKING QUANTITY

SIZE

CODE

THICKNESS

CLASSIFICATION

TAPE WIDTH

QUANTITY PER REEL

Ø 180 MM / 7 INCH

Ø 330 MM / 13 INCH

Paper

Blister

Paper

Blister

0201

0.3 ± 0.03 mm

8 mm

15,000

---

50,000

---

0402

0.5 ± 0.05 mm

8 mm

10,000

---

50,000

---

0603

0.8 ± 0.1 mm

8 mm

4,000

---

15,000

---

0805/0508

0.6 ± 0.1 mm

8 mm

4,000

---

20,000

---

0.85 ± 0.1 mm

8 mm

4,000

---

15,000

---

1.25 ± 0.2 mm

8 mm

---

3,000

---

10,000

1206/0612

0.6 ± 0.1 mm

8 mm

4,000

---

20,000

---

0.85 ± 0.1 mm

8 mm

4,000

---

15,000

---

1.0/1.15 ± 0.1 mm

8 mm

---

3,000

---

10,000

1.25 ± 0.2 mm

8 mm

---

3,000

---

10,000

1.6 ± 0.2 mm

8 mm

---

2,000

---

10,000

1210

0.85 ± 0.1 mm

8 mm

---

4,000

---

10,000

1.15 ± 0.1 mm

8 mm

---

3,000

---

10,000

1.25 ± 0.2 mm

8 mm

---

3,000

---

10,000

1812

0.6 / 0.85± 0.1 mm

12 mm

---

2,000

---

1.15± 0.1 mm

12 mm

---

1,000

---

1.25± 0.2 mm

12 mm

---

1,000

---

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

14

24

Product specification

ELECTRICAL CHARACTERISTICS

N

NP

P0

0/

/X

X7

7R

R

D

DI

IE

EL

LE

EC

CT

TR

RI

IC

C

CA

AP

PA

AC

CI

IT

TO

OR

RS

S;

;

N

NI

I/

/S

SI

IN

N

T

TE

ER

RM

MI

IN

NA

AT

TI

IO

ON

NS

S

Unless otherwise specified, all test and measurements shall be made under standard atmospheric conditions

for testing as given in 5.3 of IEC 60068-1:

- Temperature: 15 °C to 35 °C

- Relative humidity: 25% to 75%

- Air pressure: 86 kPa to 106 kPa

Before the measurements are made, the capacitor shall be stored at the measuring temperature for a time

sufficient to allow the entire capacitor to reach this temperature.

The period as prescribed for recovery at the end of a test is normally sufficient for this purpose.

Table 14

DESCRIPTION

VALUE

Capacitance range

0.2 pF to 2.2 µF

Capacitance tolerance

NP0

C < 10 pF

± 0.1 pF, ± 0.25 pF, ± 0.5 pF

C ≥ 10 pF

± 1%, ± 2%, ± 5%

X7R

±5% (1), ±10%, ± 20%

Dissipation factor (D.F.)

NP0

C < 30 pF

≤ 1 / ( 400 + 20C )

C ≥ 30 pF

≤ 0.1 %

X7R

0201

0402

0603

0805

1206

1210

1812

0508

(Array)

0612

(Array)

≤10V

220pF to 100nF

1nF to 1uF

1nF to 2.2uF

22nF to 2.2uF

100nF to 1uF

≤ 5%

≤ 10%

16V

220pF to 22nF

1nF to 220nF

1nF to 470nF

22nF to 1uF

100nF to 1uF

1nF to 10nF

220pF to 47nF

≤ 3.5%

27nF to 100nF

470nF to 1uF

680nF to 2.2uF

2.2 uF

15nF to 100nF

≤ 5%

25V

100pF to 470pF

220pF to 10nF

1nF to 39nF

1nF to 180nF

22nF to 680nF

100nF to 1uF

1nF to 10nF

220pF to 47nF

≤ 2.5%

12nF to 47nF

47nF to 220nF

220nF to 470nF

1uF

≤ 3.5%

560pF to 10nF

27nF to 100nF

1uF

680nF to 1uF

2.2 uF

≤ 5%

50V

100pF to 470pF

220pF to 10nF

1nF to 39nF

1nF to 180nF

22nF to 470nF

100nF to 1uF

470nF to 1uF

1nF

220pF to 10nF

≤ 2.5%

47nF to 100nF

220nF to 470nF

≤ 3.5%

680nF to 1uF

680nF to 2.2uF

2.2uF

≤ 5%

560pF to 1nF

4.7uF

≤ 10%

100V

220pF to 1.5nF

1nF to 10nF

1nF to 100nF

22nF to 470nF

100nF to 220nF

470nF to 1uF

≤ 2.5%

12nF to 47nF

680nF to 2.2uF

330nF to 2.2uF

≤ 5%

250V

1nF to 22nF

22nF to 100nF

100nF

≤ 2.5%

500V

1nF to 4.7nF

≤ 2.5%

Insulation resistance after 1 minute at Ur (DC)

IR ≥ 10 GΩ or I.R × C ≥ 500 seconds whichever is less

Maximum capacitance change as a function of temperature

(temperature characteristic/coefficient):

NP0

± 30 ppm/°C

X7R

± 15%

Operating temperature range:

NP0/X7R

–55 °C to +125 °C

NOTE

1. Capacitance tolerance ±5% doesn't available for X7R full product range, please contact local sales force before order

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

15

24

Product specification

SOLDERING CONDITIONS

The lead free MLCCs are able to stand the reflow soldering conditions as below:

 Temperature: above 220 °C

 Endurance: 95 to 120 seconds

 Cycles: 3 times

The test of "soldering heat resistance" is carried out in accordance with the schedule of "MIL-STD-202F-method 210F", "The robust

construction of chip capacitors allows them to be completely immersed in a solder bath of 270 °C for 10 seconds". Therefore, it is possible

to mount MLCCs on one side of a PCB and other discrete components on the reverse (mixed PCBs). Surface Mount Capacitors are tested

for solderability at 245 °C during 2 seconds. The test condition for no leaching is 260°C for 30 seconds.

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Mounting

IEC 60384-

21/22

4.3

The capacitors may be mounted on printed-circuit boards or

ceramic substrates

No visible damage

Capacitance

IEC 60384-

21/22

4.5.1

Class 1:

At 20 °C, 24 hours after annealing

f = 1 MHz for C ≤ 1nF, measuring at voltage 1 Vrms at 20 °C

f = 1 KHz for C > 1nF, measuring at voltage 1 Vrms at 20 °C

Class 2:

At 20 °C, 24 hours after annealing

f = 1 KHz, measuring at voltage 1 Vrms at 20 °C

Within specified tolerance

Dissipation

Factor (D.F.)

IEC 60384-

21/22

4.5.2

Class 1:

At 20 °C, 24 hours after annealing

f = 1 MHz for C ≤ 1nF, measuring at voltage 1 Vrms at 20 °C

f = 1 KHz for C > 1nF, measuring at voltage 1 Vrms at 20 °C

Class 2:

At 20 °C, 24 hours after annealing

f = 1 KHz, measuring at voltage 1 Vrms at 20 °C

In accordance with

specification

Insulation

Resistance

IEC 60384-

21/22

4.5.3

At Ur (DC) for 1 minute

In accordance with

specification

SOLDERING RECOMMENDATION

Table 15

SOLDERING

METHOD

SIZE

0402

0603

0805

1206

≥ 1210

Reflow

≥ 0.1 µF

≥ 1.0 µF

≥ 2.2 µF

≥ 4.7 µF

Reflow only

Reflow/Wave

< 0.1 µF

< 1.0 µF

< 2.2 µF

< 4.7 µF

---

TESTS AND REQUIREMENTS

Table 16 Test procedures and requirements

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

16

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Temperature

coefficient

4.6

Capacitance shall be measured by the steps shown in the

following table.

The capacitance change should be measured after 5 min at

each specified temperature stage.

Step

Temperature(℃)

a

25± 2

b

Lower temperature± 3℃

c

25± 2

d

Upper Temperature± 2℃

e

25± 2

(1) Class I

Temperature Coefficient shall be calculated from the formula

as below

Temp, Coefficient =

6

10

T xC1

C1-C2 

Δ

[ppm/℃]

C1: Capacitance at step c

C2: Capacitance at 125℃

∆T: 100℃(=125℃-25℃)

(2) Class II

Capacitance Change shall be calculated from the formula as

below

∆C =

C1

C1-C2

x 100%

C1: Capacitance at step c

C2: Capacitance at step b or d

Class1:

∆ C/C: ± 30ppm

Class2:

X7R: ∆ C/C: ±15%

Class2:

X7R/X5R: ∆ C/C: ±15%

High

Temperature

Exposure

AEC-Q200

3

Unpowered ; 1000hours @ T=150℃

Measurement at 24± 2 hours after test conclusion.

No visual damage

ΔC/C：

Class1:

NP0: within ± 0.5% or 0.5 pF

whichever is greater

Class2:

X7R: ± 10%

D.F.:

within initial specified value

IR:

within initial specified value

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

17

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Temperature

Cycling

AEC-Q200

4

Preconditioning;

150 +0/–10 °C for 1 hour, then keep for

24 ± 1 hours at room temperature

1000 cycles with following detail:

30 minutes at lower category temperature

30 minutes at upper category temperature

Recovery time 24 ± 2 hours

No visual damage

∆C/C

Class1:

NP0: Within ± 1% or 0.5pF,

whichever is greater.

Class2:

X7R: ±10%

D.F. meet initial specified value

IR meet initial specified value

Destructive

Physical Analysis

AEC-Q200

5

10ea X 3 lots.

Note: Only applies to SMD ceramics.

Electrical test not required.

Moisture

Resistance

AEC-Q200

6

T=24 hrs/per cycle; 10 continuous cycles unpowered.

Measurement at 24 ± 2 hours after test condition.

No visual damage

∆C/C

NP0: Within ± 3% or 3 pF,

whichever is greater

X7R: ± 15%

D.F.

Within initial specified value

IR

NP0: ≥ 10,000 MΩ

X7R: Meet initial specified

value

Fig. 4 Moisture resistant

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

18

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Biased Humidity

AEC-Q200

7

1. Preconditioning, class 2 only:

150 +0/-10 °C /1 hour, then keep for

24 ± 1 hour at room temp

2. Initial measure:

Parameter: IR

Measuring voltage: 1.5V ± 0.1 VDC

Note: Series with 100 KΩ & 6.8 KΩ

3. Test condition:

85 °C, 85% R.H. connected with 100 KΩ resistor, applied

1.5V/Ur for 1,000 hours.

4. Recovery:

Class1: 6 to 24 hours

Class2: 24 ± 2 hours

5. Final measure: IR

No visual damage after

recovery

Initial requirement:

Class1:

- Connected to 100 KΩ:

C ≤ 10 nF: I.R ≥ 10,000 MΩ

or

C > 10 nF: (I.R-100 KΩ) x C

≥ 100s.

- Connected to 6.8 KΩ:

C ≤ 10 nF: I.R ≥ 10,000 MΩ

or

C > 10 nF: (I.R-6.8 KΩ) x C

≥ 100s.

Class2:

- Connected to 100 KΩ:

C ≤ 25 nF: I.R ≥ 4,000 MΩ or

C > 25 nF: (I.R-100 KΩ) x C

≥ 100s.

- Connected to 6.8 KΩ:

C ≤ 25 nF: I.R ≥ 10,000 MΩ

or

C > 25 nF: (I.R-6.8 KΩ) x C

≥ 100s.

Final measurement:

The insulation resistance shall

be greater than 0.1 time initial

value.

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

19

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Operational Life

AEC-Q200

8

1. Preconditioning, class 2 only:

150 +0/-10 °C /1 hour, then keep for

24 ± 1 hour at room temp

2. Initial measure:

Spec: refer to initial spec C, D, IR

3. Endurance test:

Temperature: X7R: 125 °C

Specified stress voltage applied for 1,000 hours:

Applied 2.0 x Ur for general products

Applied 1.5 x Ur for high cap. Products

High voltage series follows with below

stress condition:

Applied 1.5 x Ur for 200V, 250V series

Applied 1.3 x Ur for 500V, 630V series

Applied 1.2 x Ur for 1KV, 2KV, 3KV series

4. Recovery time: 24 ± 2 hours

5. Final measure: C, D, IR

Note: If the capacitance value is less than the minimum value

permitted, then after the other measurements have been

made the capacitor shall be preconditioned according to “IEC

60384 4.1” and then the requirement shall be met.

No visual damage

∆C/C

NP0: Within ± 2% or 1 pF,

whichever is greater

X7R: ± 15%

D.F.

NP0: ≤ 2 x specified value.

X7R: ≤ 16V: ≤ 7% or specified

value whichever is greater

≥ 25V: ≤ 5% or specified

value whichever is greater

IR

NP0: ≥ 4,000 MΩ or IR x Cr ≥

40s whichever is less

X7R: ≥ 1,000 MΩ or IRx Cr ≥

50s whichever is less

External Visual

AEC-Q200

9

Any applicable method using × 10 magnification

In accordance with

specification

Physical

Dimension

AEC-Q200

10

Verify physical dimensions to the applicable device

specification.

In accordance with

specification

Mechanical

Shock

AEC-Q200

13

Three shocks in each direction shall be applied along the three

mutually perpendicular axes of the test specimen (18 shocks)

Peak value: 1,500 g’s

Duration: 0.5 ms

Velocity change: 15.4 ft/s

Waveform: Half-sin

∆C/C

NP0: Within ± 0.5% or 0.5 pF,

whichever is greater

X7R: ± 10%

D.F.

Within initial specified value

IR

Within initial specified value

Vibration

AEC-Q200

14

5 g’s for 20 minutes, 12 cycles each of 3 orientations.

Note:

Use 8” x 5” PCB. 0.31” thick 7 secure points on one long side

and 2 secure points at corners of opposite sides. Parts

mounted within 2” from any secure point. Test from

10-2000 Hz.

∆C/C

NP0: Within ± 0.5% or 0.5 pF,

whichever is greater

X7R: ± 10%

D.F: meet initial specified value

IR meet initial specified value

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

20

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Resistance to

Soldering Heat

AEC-Q200

15

Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1

hours at room temperature

Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute

Preheating: for size >1206: 100 °C to 120 °C for 1 minute

and 170 °C to 200 °C for 1 minute

Solder bath temperature: 260 ± 5 °C

Dipping time: 10 ± 0.5 seconds

Recovery time: 24 ±2 hours

Dissolution of the end face

plating shall not exceed 25% of

the length of the edge

concerned

∆C/C

Class1:

NP0: Within ± 1% or 0.5 pF,

whichever is greater.

Class2:

X7R: ± 10%

D.F. within initial specified

value

IR within initial specified value

Thermal Shock

AEC-Q200

16

1. Preconditioning, class 2 only:

150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room

temp

2. Initial measure:

Spec: refer to initial spec C, D, IR

3. Rapid change of temperature test:

NP0/X7R: -55 °C to +125 °C; 300 cycles

15 minutes at lower category temperature; 15 minutes at

upper category temperature.

4. Recovery time:

Class1: 6 to 24 hours

Class2: 24 ± 2 hours

5. Final measure: C, D, IR

No visual damage

∆C/C

NP0: Within ± 1% or 1 pF,

whichever is greater

X7R: ± 15%

D.F: meet initial specified value

IR meet initial specified value

ESD

AEC-Q200

17

Per AEC-Q200-002

A component passes a voltage

level if all components stressed

at that voltage level pass.

Solderability

AEC-Q200

18

Preheated to a temperature of 80 °C to 140 °C and

maintained for 30 seconds to 60 seconds.

Test conditions for lead containing solder alloy

Temperature: 235 ± 5 °C

Dipping time: 2 ± 0.2 seconds

Depth of immersion: 10 mm

Alloy Composition: 60/40 Sn/Pb

Number of immersions: 1

Test conditions for lead-free containing solder alloy

Temperature: 245 ± 5 °C

Dipping time: 3 ± 0.3 seconds

Depth of immersion: 10 mm

Alloy Composition: SAC305

Number of immersions: 1

The solder should cover over

95% of the critical area of each

termination.

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

21

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Electrical

Characterization

AEC-Q200

19

Parametrically test per lot and sample size requirements,

summary to show Min, Max, Mean and Standard deviation at

room as well as Min and Max operating temperatures.

∆C/C

Class 1:

NP0: ± 30 ppm/°C

Class2:

X7R: ± 15%

Class 1:

NP0: -55 °C to +125 °C

Normal temperature: 20 °C

Class 2:

X7R: -55 °C to +125 °C

Normal temperature: 20 °C

Board Flex

AEC-Q200

21

Part mounted on a 100 mm X 40 mm FR4 PCB board, which

is 1.6 ± 0.2 mm thick and has a layer-thickness 35 µm ± 10

µm.

Part should be mounted using the following soldering reflow

profile.

Conditions:

Class1:

Bending 3 mm at a rate of 1 mm/s, radius jig 340 mm

Class2:

Bending 2 mm at a rate of 1 mm/s, radius jig 340 mm

Test Substrate:

100

40

b

C

a

4.5 YNSC147

unit: mm

No visible damage

∆C/C

Class1:

NP0: Within ± 1% or 0.5 pF,

whichever is greater

Class2:

X7R: ± 10%

Dimension(mm)

Type

a

b

c

0201

0.3

0.9

0.3

0402

0.4

1.5

0.5

0603

1.0

3.0

1.2

0805

1.2

4.0

1.65

1206

2.2

5.0

1.65

1210

2.2

5.0

2.0

1808

3.5

7.0

3.7

Terminal

Strength

AEC-Q200

22

With the component mounted on a PCB obtained with the

device to be tested, apply a 17.7N (1.8Kg) force to the side of

a device being tested.

This force shall be applied for 60+1 seconds.

Also the force shall be applied gradually as not to apply a

shock to the component being tested.

* Apply 2N force for 0402 size.

Magnification of 20X or greater

may be employed for

inspection of the mechanical

integrity of the device body,

terminals and body/terminal

junction.

Before, during and after the

test, the device shall comply

with all electrical requirements

stated in this specification.

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

22

24

Product specification

TEST

TEST METHOD

PROCEDURE

REQUIREMENTS

Beam Load Test

AEC-Q200

23

Place the part in the beam load fixture. Apply a force until the

part breaks or the minimum acceptable force level required in

the user specification(s) is attained.

≤ 0805

Thickness > 0.5mm: 20N

Thickness ≤ 0.5mm: 8N

≥ 1206

Thickness ≥1.25 mm: 54N

Thickness < 1.25 mm: 15N

Voltage Proof

1. Specified stress voltage applied for 1~5 seconds

2. Ur ≤ 100 V: series applied 2.5 Ur

3. 100 V < Ur ≤ 200 V series applied (1.5 Ur + 100)

4. 200 V < Ur ≤ 500 V series applied (1.3 Ur + 100)

5. Ur > 500 V: 1.3 Ur

6. Ur ≥ 1000 V: 1.2 Ur

Charge/Discharge current is less than 50 mA

No breakdown or flashover

Note: Classify the components according to the highest ESD voltage level survived during

ESD testing.

Fig. 5 Passive component HBM ESD test flow diagram (DC = Direct Contact Discharge, AD = Air Discharge)

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

23

24

Product specification

REVISION HISTORY

REVISION

DATE

CHANGE NOTIFICATION

DESCRIPTION

Version 11

Jun. 29, 2018

-

- Add 0201 NPO 25V/ 50V, 0.2pF to 33pF, Add 0402 NPO 50V 270pF to

1nF, Add 0805 X7R 25V 2.2uF

Version 10

May. 2, 2018

-

- Add 0603 NPO 100V 820pF to 1nF,

- Add 0805 NPO 50V to 100V, 1.2nF to 10nF,

- Add 0805 X7R 16V 2.2uF, 50V 680nF to 1uF,

- Add 1206 X7R 100V 330nF to 2.2uF, 250V 33nF to 100nF

Version 9

Mar. 22, 2018

-

- Add 0402 X7R 100nF 25~50V

Version 8

Nov. 22, 2017

-

- Add X7R/0201/25V/100pF~10nF

Version 7

Jul. 7, 2017

-

- Add X7R/0805/330nF to 470nF/50V, X7R/1206/10uF/6.3V

Version 6

Mar. 31, 2017

-

- Add NPO/0603/1nF/50V, X7R/0603/1uF/10V, X7R/0603/470nF/16V,

X7R/0603/220nF/25V

Version 5

Nov. 15, 2016

-

- Add Soldering Condition

Version 4

Jun. 14, 2016

-

- Add X7R/0805/2.2uF/10V and NPO/1206/1.2nF to 1.5nF/250V

Version 3

Jul. 21, 2015

-

- Tests and Requirements update

Version 2

Jul. 17, 2014

-

- Tests and Requirements update

Version 1

Apr. 19, 2013

-

- Capacitance range update

Version 0

Dec. 25, 2012

-

- New

Automotive grade

NP0/X7R

6.3 V to 630 V

www.yageo.com

Feb. 26, 2019 V.12

Surface-Mount Ceramic Multilayer Capacitors

24

Product specification

LEGAL DISCLAIMER

Yageo, its distributors and agents (collectively, “Yageo”), hereby disclaims any and all liabilities for any errors,

inaccuracies or incompleteness contained in any product related information, including but not limited to

product specifications, datasheets, pictures and/or graphics. Yageo may make changes, mod ifications and/or

improvements to product related information at any time and without notice.

Yageo makes no representation, warranty, and/or guarantee about the fitness of its products for any particular

purpose or the continuing production of any of its products. To the maximum extent permitted by law, Yageo

disclaims (i) any and all liability arising out of the application or use of any Yageo product, (ii) any and all

liability, including without limitation special, consequential or incidental damages, and (iii) any and all implied

warranties, including warranties of fitness for a particular purpose, non -infringement and merchantability.

Yageo statements regarding the suitability of products for certain types of applications are based on Yageo’s

knowledge of typical operating conditions for such types of applications in a generic nature. Such statements

are neither binding statements of Yageo nor intended to constitute any warranty concerning the suitability for a

specific customer application or use. They are intended for use only by customers with requisite knowledge and

experience for determining whether Yageo products are the correct products for their application or use. In

addition, unpredicatable and isolated cases of product failure may still occ ur, therefore, customer application or

use of Yageo products which requires higher degree of reliability or safety, shall employ additional protective

safeguard measures to ensure that product failure would not result in personal injury or property damage.

Yageo products are not designed for application or use in medical, life -saving, or life-sustaining devices or for

any other application or use in which the failure of Yageo products could result in personal injury or death.

Customers using or selling Yageo products not expressly indicated for above-mentioned purposes shall do so at

their own risk and agree to fully indemnify Yageo and hold Yageo harmless.

Information provided here is intended to indicate product specifications only. Yageo reserves all the rights for

revising this content without further notification, as long as products are unchanged. Any product change will

be announced by PCN.